Effect of Oxalate Desensitizer on Microshear Bond Strength of Adhesive System to Dentin
Purpose: The purpose of this study was to evaluate effect of oxalate desensitizer on microshear bond strength between dentin and adhesive system.
Material and methods: Ten extracted human molar teeth without any caries or restoration were collected. Teeth were cut at cervical area to make dentin disc and then grind into flat plane at both buccal and lingual aspect parallel to outer surface of the tooth into the dentin below dentino-enamel junction (DEJ) 1mm. The specimens were devided to experimental and control group. BisBlock™ (Bisco), oxalate desensitizer, was applied on dentin treated with phosphoric acid in experimental group. For control group, the desensitizer was not applied. Then Adper™ Single bond 2 (3M ESPE) was applied to the treated dentin surface to bond with resincomposite, Filtek™ Z350 (3M ESPE), in 0.7 mm diameter and 1.2 mm thick mold. The specimens were stored in distilled water 37°C for 24 hours before microshear bond strength was measured using a universal testing machine. The data were analysed statistically using Independent t Test.
Result: The means microshear bond strength of oxalate desensitizer experimental group and control group were 19.95±6.03 MPa and 17.03±9.33 MPa. There was no significant different between oxalate and control group.
Conclusion: Within the limitation of this study, oxalate desensitizer did not reduce microshear bond strength between dentin and on adhesive system.
1. Brännström M, Astrom A.The hydrodynamics of the dentine; its possible relationship to dentinal pain. Int Dent J 1972; 22(2): 219-227.
2. เฉลิมพล ลี้วิโรจน์, ศิริวิมล ศรีสวัสดิ์. เสียวฟันแก้ไขอย่างไรดี (ตอนที่ 2). ว ทันต หัตถการ 2550; 7(2): 5-10.
3. Trowbridge HO, Silver DR. A review of current approaches to in-office management of tooth hypersensitivity. Dent Clin North Am 1990; 31(3): 561-582.
4. Pashley DH. Dentin permeability, dentin sensitivity, and treatment through tubule occlusion. J Endod 1986; 12(10): 465-474.
5. Pashley DH, Carvalho RM, Pereira JC, Villanueva R, Tay FR. The use of oxalate to reduce dentin permeability under adhesive restorations. Am J Dent 2001; 14(2): 89-94.
6. Bartold PM. Dentinal hypersensitivity: a review. Aust Dent J 2006; 51(3): 212-218.
7. Kerns DG, Scheidt MJ, Pashley DH, Horner JA, Strong SL, Van Dyke TE. Dentinal tubule occlusion and root hypersensitivity. J Periodontol 1991; 62(7): 421-428.
8. Gillam DG, Mordan NJ, Sinodinou AD, Tang JY, Knowles JC, Gibson IR. The effects of oxalate-containing products on the exposed dentine surface: an SEM investigation. J Oral Rehabil 2001; 28(11): 1037-1044.
9. Pereira JC, Segala AD, Gillam DG. Effect of desensitizing agents on the hydraulic conductance of human dentin subjected to different surface pre-treatments-an in vitro study. Dent Mater 2005; 21(2): 129-138.
10. Greenhill JD, Pashley DH. The effect of desensitizing agents on the hydraulic conductance of human dentin in vitro. J Dent Res 1981; 60(3): 686-698.
11. Pashley DH, Galloway SE. The effects of oxalate treatment on the smear layer of ground surfaces of human dentine. Arch Oral Biol 1985; 30(10): 731-737.
12. Camps J, Pizant S, Dejou J, Franquin JC. Effectes of desensitizing agents on human dentin permeability. Am J Dent 1998; 11(6): 286-290.
13. Hirvonen TJ, Narhi MV, Hakumaki MO. The excitability of dog pulp nerves in relation to the condition of dentine surface. J Endod 1984; 10(7): 294-298.
14. Muzzin KB, Johnson R. Effects of potassium oxalate on dentin hypersensitivity in vivo. J Periodontol 1989; 60(3): 151-158.
15. Cuenin MF, Scheidt MJ, O’Neal RB, et al. An in vivo study of dentin sensitivity: the relation of dentin sensitivity and the patency of dentin tubules. J Periodontol 1991; 62(11): 668-673.
16. Pashley El, Tao L, Pashley DH. Effects of oxalate on dentin bonding. Am J Dent 1993; 6(3): 116-118.
17. Seara SF, Erthal BS, Ribeiro M, Kroll L, Pereira GD. The influence of a dentin desensitizer on the microtensile bond strength of two bonding systems. Oper Dent 2002; 27(2): 154-60.
18. Pereira PN, Okuda M, Sano H, Yoshikawa T, Burrow MF, Tagami J. Effect of intrinsic wetness and reginol difference on dentin bond strength. Dent Mater 1999; 15(1): 46-53.
19. Opdam NJ, Feilzer AJ, Roeters JJ, Smale I. Class I occlusal composite resin restorations: in vivo post-operative sensitivity, wall adaptation, and microleakage. Am J Dent 1998; 11(5): 229-234.
20. Akpata ES, Sadiq W. Post-operative sensitivity in glass-ionomer versus adhesive resin-lined posterior composites. Am J Dent 2001; 14(1): 34-38.
21. Tay FR, Pashley DH, Mark TF, Carvalho RM, Lai SC, Suh BI. Integrating oxalate desensitizers with total-etch two-step adhesive. J Dent Res 2003; 82(9): 703-707.
22. Yiu CK, King NM, Suh BI, et al. Incompatibility of oxalate desensitizers with acidic, fluoride-containing total-etch adhesives. J Dent Res 2005; 84(8): 730-735.
23. Vachiramon V, Vargas MA, Pashley DH, et al. Effects of oxalate on dentin bond after 3- month simulated pupal pressure. J Dent 2008; 36(3): 178-185.
24. Inoue M, Finger WJ, Mueller M. Effect of filler content of restorative resins on retentive strength to acid-conditioned enamel. Am J Dent 1994; 7(3): 161-166.
25. Jacobsen PL, Bruce G. Clinical dentin hypersensitivity:understanding the causes and prescribing a treatment. J Contemp Dent Pract 2001; 2(1): 1-12.
26. Akca T, Yazici AR, Celik C, Ozgunaltay G, Dayangac B. The effect of desensitizing treatments on the bond strength of resincomposite to dentin mediated by a self-etching primer. Oper Dent 2007; 32(5): 451-456.
27. Tavares M, DePaola PF, Soparkar P. Using a fluoride-releasing resin to reduce cervical sensitivity. J Am Dent Assoc 1994; 125(10): 1337-1342.
28. Gillam DG, Coventry JF, Manning RH, Newman HN, Bulman JS. Comparison of two desensitizing agents for the treatment of cervical dentine sensitivity. Endod Dent Traumatol 1997; 13(1): 36-39.
29. Pamir T, Dalgar H, Onal B. Clinical evaluation of three desensitizing agents in relieving dentin hypersensitivity. Oper Dent 2007; 32(6): 544-548.
30. Hanks CT, Wataha JC, Parsell RR, Strawn SE, Fat JC. Permeability of biological and synthetic molecules through dentine. J Oral Rehabil 1994; 21(4): 475-487.
31. Gerzina TM, Hume WR. Effect of hydrostatic
pressure on the diffusion of monomers through
dentin in vivo. J Dent Res 1995; 74(1): 369-
373.